Rotomolding Grade LLDPE Foaming Agent Material Compounding Powder, LLD484P minangka bubuk rotoplastik sing dimodifikasi LLDPE kanthi rasio foaming 4. Suhu wiwitan kira-kira 150 ℃, lan suhu busa paling apik kira-kira 180 ℃.
Rotomolding Grade LLDPE Foaming Agent Material Compounding Powder, LLD484P minangka bubuk rotoplastik sing dimodifikasi LLDPE kanthi rasio foaming 4. Suhu wiwitan kira-kira 150 ℃, lan suhu busa paling apik kira-kira 180 ℃.
Formulir |
● Komersial: aktif |
kasedhiyan |
● AS |
Aditif |
● HS |
Fitur |
|
Migunakake |
● Isi |
Ratings agensi |
● ROHS |
Kemasan |
● 20Kg / packing |
Urip beting |
● 1 taun saka tanggal produksi |
Lembar data | Nilai Khas | Unit | Metode Tes |
fisik | |||
Kapadhetan | - | g/cm3 | ISO 1183 |
Akeh Kapadhetan | 0.250 | g/cm3 | ISO60 |
Indeks Leleh (190 ℃, 2,16Kg) | 3.2 | g / 10 min | ISO 1133 |
Laju Aliran Kering | 24 | s / 100 g | ARM |
E.S.C.R. | - | h | ASTM D1693 |
Titik Lebur | 119 | ℃ | ISO 11357 |
Mekanik | |||
Kekuwatan Tensile ing Ngasilake | 6 | MPa | ISO527 |
Tensile Elongation ing Ngasilake | 50 | % | ISO527 |
Modulus lentur | 210 | MPa | ISO 178 |
Kekuwatan impact | - | J/mm | ARM |
Hardness, Shore D | - | D | ISO868 |
Thermal | |||
Suhu defleksi (0.45MPa) | - | ℃ | ISO75 |
Vicat Softening Point | - | ℃ | ISO 306 |
Suhu Brittleness | - | ℃ | ISO974 |
tuwa | |||
Wektu Induksi Oksidasi | 20 | min | ISO 11357 |
Rating UV | - | h | ASTM 2565 |
Liyane | |||
Resistivitas lumahing | - | Ω | IEC60093 |
Flame retardant | - | sasmita | UL-94 |
Data pandhuan iki khas saka data produk merek, lan ora bisa digunakake minangka indikator jaminan kualitas supplier.